Contact
Tel: 18037961302
Sales hot line ( 24 hours  service): 18037961302

E-Mail: firstfurnace@gmail.com

whatsapp:+8618037961302

Adress: Luoxin Industrial Park, Luoyang, Henan
  • Products
  • Gear hardening machine

    Large diameter steel pipe quen

    Piston rod quenching and tempe

    Hand-held induction heater

    Grinding rod quenching and tem

    Induction forging machine

    induction heating machine 

    Induction heater

    High frequency induction heate

    Super audio induction heating

    Super audio induction heating

    Guideway quenching integrated

    Quenching equipment for machin

    Round steel end heating furnac

    Steel pipe heat treatment prod

    Square steel quenching and tem

    Sucker rod quenching and tempe

    Thickened petroleum steel pipe

    Round steel quenching and temp

    Steel pipe quenching and tempe

    Steel plate quenching and temp

    Induction Hardening Machine&nb

    Flywheel ring gear high freque

    Oil drill pipe quenching and t

    Iron induction furnace

    Aluminum melting furnace

    Copper melting furnace

    Small steel melting furnace

    Electric furnace technical information(技术)
        

    How about the performance of medium frequency induction heating surface hardening?

    1. Surface hardness: The surface hardness of workpieces that are surface-quenched by high- and medium-frequency induction heating is often 2 to 3 units (HRC) higher than ordinary quenching.

    2. Wear resistance: The wear resistance of the workpiece after high frequency quenching is higher than that of ordinary quenching. This is mainly due to the combination of small martensite grains in the hardened layer, high carbide dispersion, high hardness, and high surface compressive stress.

    3. Fatigue strength: high and medium frequency surface quenching greatly improves fatigue strength and reduces notch sensitivity. For the workpiece of the same material, the depth of the hardened layer is within a certain range. As the depth of the hardened layer increases, the fatigue strength increases, but when the depth of the hardened layer is too deep, the surface layer is compressive, so the fatigue strength decreases when the depth of the hardened layer increases. Increased brittleness. Generally, the depth of the hardened layer is δ=(10~20)%D. More appropriate, where D. Is the effective diameter of the workpiece


    Copyright© 2007-2013 songdao Electric furnace manufacturing Co,.Ltd All Rights Reserved
    Tel:18037961302 Sales hot line ( 24 hours service): 18037961302
    E-Mail:firstfurnace@gmail.com
    Adress: Luoxin Industrial Park, Luoyang, Henan