  • 0.5T intermediate frequency me

    Medium Frequency Induction Mel

    250kg induction melting f

    500kg medium frequency in

    5T Medium Frequency Induction

     5T Induction Meltin

     500kg induction mel

    induction melting furnace

    3T medium frequency induction

    2T frequency induction me

    1T Medium Frequency Induction

    Bar heating furnace

    300KG electromagnetic melting

    250 KG electromagnet

    200 KG electromagnet

    silver melting furnace

    Brass melting Furnace

    atomization milling equipment

    Platinum melting furnace

    Selection of common spare part

    Medium frequency copper meltin

    scrap copper melting furnace

    800kg electromagnetic

    600KG electromagnetic copper m

    500KG electromagnetic

    400KG electromagnetic copper m

    350KG electromagnetic copper m

    300KG electromagnetic copper m

    smelting equipment

    product description

        

     The medium frequency induction furnace refining technology can transform the medium frequency induction furnace from " chemical steel " to steelmaking when smelting alloy steel and special steel, so that its quality index reaches the current AOD, VOD, LF refining furnace, VD vacuum degassing The quality level of the furnace is an important way to improve the quality and reduce waste products for small and medium-sized furnace smelting and casting enterprises. It is a production process with less investment, quick effect, low cost and high quality. It is an energy-saving and consumption-reducing process. The environmentally friendly production process is a process of production. The technology is based on different steel types, different requirements, different gases through the intermediate frequency induction furnace to refine the control gas flow of the gas supply system, to achieve the removal of slag inclusions and  O   N   H  content or special requirements Nitrogen is added to the decarburization and nitrogen-containing steel.

        The principle of argon refining in medium frequency induction furnace : Induction furnace bottom argon refining process is completed in pre-deoxidation of molten steel. After sampling and analysis of additional alloying materials, high-purity argon gas is introduced into the molten steel through a gas diffuser installed at the bottom of the furnace ( It will only ventilate without oozing the molten steel. When argon passes through the gas diffuser, the dispersion is higher and the bubble flow has a larger rising speed. Countless bubbles passing through the molten steel will bring  O   N   H  and inclusions out of the molten steel to achieve refining.

    Each argon bubble inside the molten steel is a small " vacuum chamber " that does not contain  O   N   H  argon gas bubbles, that is, the partial pressure of these gases in the argon bubble is equal to zero.

    When the argon bubble with a high partial pressure passes through the molten steel, the O ー N   H  in the dissolved state and the CO in the non-dissolved state will automatically enter the argon bubble and rise as the bubble rises. Spilling, in order to achieve the purpose of degassing, to achieve the purpose of removing non-metallic inclusions.

    Since the beginning of August 2011 , the medium frequency induction furnace smelting has been carried out . The purity of the steel after refining has been greatly improved. The contrast of inclusions before and after refining has been significantly reduced, and the gas content has been greatly reduced. The specific comparison is as follows:

    1 , the effect of argon refining to remove lead  pb 

    Steel grade

    Blowing Armin

    Before refining ( % )

    After refining ( %)

    Reduction rate (% )

    40

    20

    0.0087

    0.0016

    80.4

    AISI430

    19

    0.0300

    0.008

    78.2

    2 , the effect of argon refining to remove hydrogen  H 

    Steel grade

    Blowing Armin

     H ― content

    Change /10-6

    Reduction rate (% )

    Before refining ( % )

    After refining ( %)

    40

    20

    12.0

    2.8

    75.9

    AISI430

    35

    9.3

    4.51

    52.1

    2GMN13

    31

    7.9

    4.15

    50.0

    3 , inclusions:

    Microscopic evaluation method for non-metallic inclusions in steel GB10561-2005

    project

    A

    B

    C

    D

    Sulfide

    Oxide

    Silicate

    Spherical oxide

    Average before refining

    Level 1.8

    Level 1.7

    Level 1.5

    Level 2.1

    Average after refining

    Level 0.55

    Level 0.64

    Level 0.5

    0.67 level

    Average reduction by %

    69

    62

    67

    68

    The actual measurement standard fully meets the technical requirements:

    4 , the hydrogen content is less than 1.0ppm , meet the requirements of mold steel Q2.5ppm , other steel types Q3.0ppm .

    5 , the nutrient content is less than 0.0050% .

    6, after the ingot processing, ultrasonic testing reached (GB / T133515-1991) secondary standard.

    7, performance comparison of mechanical refining of stainless steel 304 and stainless steel, etc. :( GB / T328-2002)

    1) Tensile strength: refined steel refined in front 549.53Mpa 606.82Mpa improve 57.29Mpa

    2) Yield strength: 270Mpa refined steel refined in front 339.52Mpa improve 69.52Mpa

    3) maximum force: refined steel after refining before 38.46pa 49.10Mpa improve 10.64Mpa

    The technology is applied to induction furnaces and power frequency furnaces. The tonnage is 0.5T-20T furnace body. Practical use

    1, the alkaline sand MgO lining. 2 , weakly alkaline MgO + AI 2 O 3 furnace lining. 3 , neutral corundum AI 2 O 3 furnace lining.

    4 , acidic neutral AI 2 O 3 + SiO2 furnace lining. 5 , acid quartz sand furnace lining.

    This technique does not increase the smelting time, because refining is performed during the melting process of the alloy material, so that the smelting time is not extended, and thus the power consumption is not increased.

    Due to the refining of the molten steel, the quality of the product is significantly improved. And the cost has increased. Synchronous increase of 8.23 yuan per ton of steel . The improvement of steel quality, the reduction of waste, and the overall cost are still reduced.

     https://www.zplkz.com/plus/view.php?aid=509


    Copyright© 2007-2013 songdao Electric furnace manufacturing Co,.Ltd All Rights Reserved
    Tel:18037961302 Sales hot line ( 24 hours service): 18037961302
    E-Mail:firstfurnace@gmail.com
    Adress: Luoxin Industrial Park, Luoyang, Henan